2% Silver Copper Phosphor Brazing Alloy

FACTORY NAME: HZ-Ag2P
AWS 5.8: BCuP-6
EN 1044: CP105
DIN 8513: L-Ag2P
SOLIDUS: 643℃
LIQUIDUS: 788℃

Price:

$ 20.39

ꄑview：0

Service： Free samples,
Quick reply within 24 hours.
Factory self-employed,
Quality assurance.

Quick Details
Place of Origin: Anhui, China	Brand Name: HUAZHONG
Model Number: HZ-Ag2P	Material: Copper / Copper Alloy
Operating Temperature: 643℃-788℃	Operating Current: International Standard
Application: refrigeration, air-condition	Welding Current: International Standard
Product Name: Silver copper phosphor welding alloy	Type: Manufaturer Bar Solder Stick
Usages: Welding Tool	Advantage: Easy Restrike Arc

Forms:•rod•wire•strip•rings•paste•powder•proforms•particle

----------------------------------------------------------------------------------------------------------------------------------------------

Packing Details

1kg/bag 20kg/carton 1000kg/pallet

2kg/bag 20kg/carton 1000kg/pallet

International Export Packing

As your request

----------------------------------------------------------------------------------------------------------------------------------------------

Technical Sheet
HZ. NO	EN1044	AWS 5.8	DIN8513	Melting Range	Chemical Composition
HZ-Ag2P	CP105	BCuP-6	L-Ag2P	643-788℃	Ag：2% Cu:91% P:7%

----------------------------------------------------------------------------------------------------------------------------------------------

Product Description

HZ-Ag2P should not be used when joining parts that could come into contact in operation with sculptures containing medias,and should not be used on ferrous or nickel alloys,due to the formation of brittle inter metallic compounds which

will cause failure of the joint.

----------------------------------------------------------------------------------------------------------------------------------------------

Application

HZ-Ag2P is an alloy commonly used in capillary brazing and braze welding of joints in copper, brass and bronze-zinc

alloys. The phosphorus contained in the alloy acts as a fluxing agent,so that it is not necessary to use an additional flux

when brazing copper to copper ;however when joining copper based materials,flux should be used.